Nikkelilajit ja kemiallinen koostumus
| Puhdasta nikkeliä | Ni+Co | Cu | Si | Mn | C | Mg | S | Fe | Epäpuhtaudet yhteensä | UNS:n nimitys |
| ei vähempää kuin | ||||||||||
| N2 | 99.98 | 0.001 | 0.003 | .002 | .005 | .003 | .001 | .007 | .02 | |
| N4 | 99.9 | 0.015 | 0.03 | .002 | .01 | .01 | .001 | .04 | 0.1 | N02201 |
| N6 | 99.5 | 0.06 | 0.10 | .05 | .10 | .10 | .005 | .10 | 0.5 | N02200 |
| N8 | 99.0 | 0.15 | 0.15 | .20 | .20 | .10 | .015 | .30 | 1.0 | |
| DN | 99.35 | 0.06 | 0.02-0.10 | 0.05 | .02.10 | .02-.10 | .005 | .10 | 0.35 | |
| NY1 | 99.7 | 0.1 | 0.1 | - | .02 | .10 | .005 | .10 | 0.3 | |
| NY2 | 99.4 | 0.01-0.10 | 0.1 | - | - | - | 0.002-0.01 | .10 | 0.6 | |
| NY3 | 99.0 | 0.15 | 0.2 | - | 0.1 | 10 | 0.005 | .25 | 1.0 | |
| NMg0,1 | 99.6 | 0.05 | 0.02 | .05 | .05 | 0.07~0.15 | 0.005 | .07 | .40 | |
| NSI0.19 | 99.4 | 0.05 | 0.15~0.25 | .05 | .10 | .05 | 0.005 | .07 | .50 | |
Nikkelin korroosionkestävyys
Nikkeli on erityisen kestävä alkalikorroosiota vastaan ja on suhteellisen vakaa korkeassa lämpötilassa tai liekkisulatetussa alkalissa, joten sitä käytetään pääasiassa alkaliteollisuudessa. Normaalilämpötilassa etana on erittäin stabiili merivedessä, suolaliuoksessa ja orgaanisessa väliaineessa (kuten rasvahapossa, fenolissa, käymisessä jne.), eikä se kestä epäorgaanisen hapon korroosiota eikä stabiili etikkahapossa ja kevyessä hapossa.